The liquid ammonia and vacuum distillation techniques were found to be satisfactory for removing lithium from 1040 C aged T-111 (tantalum - 8-percent tungsten- 2-percent hafnium). Results of ductility tests and chemical analysis show that these two methods are adequate for removing lithium without embrittlement or contamination of the T-111. Moist air exposure of T-111 with traces of lithium on the surface produced mixed results. Some specimens were ductile; others were brittle. Brittle T-111 had an increased hydrogen content. Water removal of lithium from T-111 caused brittleness and an increased hydrogen concentration.